A wire designed for welding chemically pure aluminum products, which are subject to stringent requirements for resistance to erosion when in contact with chemically aggressive media. The deposited metal is not prone to stress corrosion cracking at operating temperatures above 65°C, has sufficiently high plastic properties that allow rolling and forming, as well as anodizing products after welding. Welding is recommended on equipment that supports MIG-pulse mode, especially for thicknesses up to 4 mm.
۱۰۷۰ is highly resistant to chemical attack and weathering. It is a relatively soft alloy that is very formable and it is used extensively in thin-gauge and foil products. It has good welding characteristics. One characteristic feature of the alloy is the bright finish obtained by anodising. Non-heat treatable.
۱۰۷۰ Pure aluminium welding wire containing more than 99.7% aluminium, it has advantages rang over good anti-corrosiveness, well heat and electronic conductivity, machinability, low strength.
And it also is kind of best choice for color-match after anodic process. You should strictly clean the oxide film on the edge of the workpiece and oil before welding, otherwise it will make bad weld produce and cause porosity, slag inclusion and other defects.
You can use a plate to hold molten metal to ensure meld form and avoid cracks. The argon arc welding of pure aluminium is used as the filler material, widely used in electrolytic aluminium bus bar and rod connections and ships, railway locomotive, chemical, food, sports equipment, electric power, etc.
Uses:
Used as pure aluminum of argon arc welding and gas welding filler material, widely used in electrolytic aluminum bus bar and a guide rod connection and electric power, chemical, food etc. industries.
Properties
- ALloy composition%: Al min 99.70
- Melting range: 658℃
- Density: 2.70g/cmm³
- Tensile strength（N/mm）: ≥۶۰
- Expansion（A5）: ≥۴۰%
Note:
۱.welding should be strict and clear the edge of the welding of the oxide film and oil, otherwise it will cause welding seam welding and cause the hole, slag and other defects.
۲ welding can be used for holding molten metal plate, in order to ensure the weld forming, and avoid hot crack.